CXT8113 natural is a high purity, high transparency, amorphous, thermoplastic polyamide, based on cycloaliphatic monomers. Compared with semi-crystalline nylon, CXT8113 avoid crystallizing by selecting specific monomers and becomes an other amorphous polymer which has high transparency. Meanwhile, CXT8113 combine the properties of semi-crystalline nylon and amorphous nylon which makes it be the first choice in the present market.
Composition PAMACM12
| ||||||||||
| Optics | Packaging | |
| Frames, Lens, Optical components etc. | Cosmetics packaging, Medical packaging, etc. | |
| Food Contact | Industry | |
| Feeder, Coffee machine, Cup, etc. | | Auto parts(oil cup, etc), Mechanical engineering. |
| Ectronic Products | Consumer Goods | |
| Headphone, Ear-Hook, etc. | Sports & Leisure, Tools & Accessories, etc. |
| Items | Unit | Test Method | Values |
| Charpy notched impact | KJ/m² | GB/T 1043-93 | 17 |
| Charpy non-notched impact | KJ/m² | GB/T 1043-93 | 25JNB |
| Tensile strength | MPa | GB/T 1040-92 | 65 |
| Elongation at break | % | GB/T 1040-92 | 160 |
| Flexural strength | MPa | GB 9341-2000 | 70 |
| Flexural modulus | MPa | GB 9341-2000 | 1780 |
| Density | g/cm³ | GB 1033-86 | 1.01 |
| Heat distortion temperature(0.45 MPa) | ºC | GB1634-79 | 135 |
| Light transmittance | % | -- | 92 |
| Shore D hardness | -- | GB 2411-80 | 83 |